Copper bars are taken as raw material and are cut into size. Some bars are bent to configuration as required. 

CAgroup can deliver any custom bar specification, according to the client’s need.

CAgroup offers a wide range of hook accessories. Hooks are added to the hanger bars per client requirements, especially in the case of anodes for Zinc Electrowinning.

CAgroup can deliver any custom bar specification, according to the client’s need.

All anodes supplied are hard-stamped with a unique identifying number, allowing traceability of that anode right back through the quality system. For each project, a full certification “passport” is supplied to the client, which includes material analysis, mechanical testing, tolerance control and conductivity performance.

Testing and certification are conducted at CAgroup in-house laboratory utilising state-of-the-art testing equipment to test material alloys, microstructure, hardness, mechanical properties and tolerance control.

Rolled anodes used in Zinc electrowinning are usually blasted according to client specifications, such as surface roughness, to ensure optimum anode conditioning.

When in use, pure lead cannot support its own weight and will creep. This creep will break the lead oxide layer on the anode surface, causing exposure of fresh lead to oxidisation and corrosion. Alloying of the lead increases the mechanical strength during use, preventing creep and thus the cracking of the oxidised surface layer and maintaining the anode shape. Lead antimony, lead tin antimony and lead silver were used for many years in copper and zinc electrowinning as alloys to provide the desired mechanical properties. With the advent of solvent extraction and electrowinning systems to produce high-purity cathode deposits, the need arose for much lower lead levels in the cathode deposit. As such, alloys with calcium were developed to reduce the level of lead deposit. As calcium lead alloys are relatively weak, tin is added to increase mechanical strength and decrease creep. Tin addition also reduces passivation when the power is interrupted.

The rolled blade and the hanger bar are joined together by lead burning consisting of a full penetration stitch weld (continuous) and then, a second fillet weld.

All assembly will be carried out on custom made jigs to ensure all anodes are concentric.

After assembly, anodes will be removed from the jigs and randomly checked for verticality.

Rolled alloys used for anodes are superior to cast anodes, as the rolling process changes the cast grain structure to produce fine uniform directional grains and reduces the corrosion rate. The rolled anode is produced from large cast slabs, which cool sufficiently slowly so that all the included air and dross generated during the pouring process are removed prior to solidification before rolling. Thus, there are no oxides, air inclusions or laminations.

The rolled anode has a much finer and more uniform grain structure than cast anodes. Corrosion occurs as a fine, uniform, thin layer.